Introduction -

TUFF COAT EP 102 Epoxy Zinc rich primer is a two-pack system enriched with metallic zinc to provide outstanding performance in highly corrosive environment. Metallic Zinc imparts Cathodic protection to the base metal and Epoxide groups react with polyamide/ Amine adduct hardener to form tough, non-convertible film at ambient temp or elevated temp. It resists photo degradation by UV light as it contains UV absorber.
TUFF COAT EPOXY ZINC RICH priming is also known as "COLD GALVANISING"

RANGE OF APPLICATION
Suitable for application as a priming coat on structural steel, pipelines, and tank exteriors of refineries, power generation plants, mining facilities bulk handling equipment and fertilizer industries etc. This can be TOP-COATED with Epoxy Paints; Polyurethane paints chlorinated rubber paints for specific applications.

KEY PROPERTIES
1. Provides excellent adhesion on blast cleaned steel work
2. Withstands 200°C dry heat
3. Excellent corrosion resistance
4. With suitable TOP-COAT it resists most salts & alkalis
5. Mild Acid & alcohol resistance (Direct immersion is not advisable)
6. Resists splash, spillage, immersion of aromatic hydrocarbon & solvents
7. Good abrasion resistance

PRODUCT DATA (Two types available)
Zinc Dust Content 62%
Mixing ratio by Volume Base: Hardener 4: 1
Pot Life 3 - 4 hrs.
Individual shelf life 8 months in sealed condition & at ambient temp.
Application by Brush, Airless spray, Roller or Conventional spray
Covering Capacity-theoretical 8 - 10 sq. m. / Lit.
Drying time at room temp Surface Dry 35-40 min.
30-350 Tack free 1.5 hrs.
Hard dry overnight
Full cure time 7days
Overcoat Interval * Recommended DFT Minimum overnight, Maximum
Min.50µ
Stoving schedule (if necessary) 120°C./30 min
Flash Point above 22°C
Finish Grey, Matt - slight sheen, rough
Packing Base 20 liter 4 liter
Hardener 5 liter 1liter
Salt Spray Resistance a. 65% zinc content - 250 hrs
b. 92% zinc content - more than 500 hrs.

APPLICATION -

Remove oil, grease and other contaminants using proper degreasing agent. For severe corrosive conditions blast clean the surface. Special care must be taken on weld areas to remove flux & spatter. The cleaned surface should be coated before it gets contaminated or applies wash primer before subsequent coat of zinc rich primer.
Stir base thoroughly then mix four parts base and one part hardener by volume to uniform consistency. Allow the mixture to mature for 20-30 min. and stir again before application & occasionally during use to prevent settling of metallic zinc.
For Brush, Roller, Airless spray application, no thinning is required. In conventional spraying, 5% to 10% thinning is recommended for ease of application.

NOTE
1) Use the mixed paint within specified pot life period
2) Do not apply at temperatures below 10° C or at high relative humidity, above 90% or during rain, fog or mist.
3) Brushes & spray equipment should be cleaned with Thinner EP-102 otherwise equipment is liable to be damaged.


Epoxy Primer - Zinc Rich 92%

Go Back to - Home / Products

Introduction -

TUFF COAT Epoxy Zinc rich primer is a two-pack system enriched with metallic zinc to provide outstanding performance in highly corrosive environment. Metallic Zinc imparts cathodic protection to the base metal and Epoxide groups react with polyamide/ Amine adduct hardener to form tough, non-convertible film at ambient temp or elevated temp. It resists photo degradation by UV light as it contains UV absorber.
TUFF COAT EPOXY ZINC RICH priming is also known as "COLD GALVANISING"

RANGE OF APPLICATION
Suitable for application as a priming coat on structural steel, pipelines, and tank exteriors of refineries, power generation plants, mining facilities bulk handling equipment and fertilizer industries etc. This can be TOP-COATED with Epoxy Paints; Polyurethane paints chlorinated rubber paints for specific applications.

KEY PROPERTIES
1. Provides excellent adhesion on blast cleaned steel work
2. Withstands 200° C dry heat
3. Excellent corrosion resistance
4. With suitable TOP-COAT it resists most salts & alkalis
5. Mild Acid & alcohol resistance (Direct immersion is not advisable)
6. Resists splash, spillage, immersion of aromatic hydrocarbon & solvents
7. Good abrasion resistance

PRODUCT DATA (Two types available)
Zinc Dust Content 92%
Mixing ratio by Volume Base: Hardener 4: 1
Pot Life 3 - 4 hrs.
Individual shelf life 8 months in sealed condition & at ambient temp.
Application by Brush, Airless spray, Roller or Conventional spray
Covering Capacity-theoretical 8 - 10 sq. m. / Lit.
Drying time at room temp Surface Dry 35-40 min.
30-350 Tack free 1.5 hrs.
Hard dry overnight
Full cure time 7days
Overcoat Interval * Recommended DFT Minimum overnight, Maximum
Min.50µ
Stoving schedule (if necessary) 120°C./30 min
Flash Point above 22°C
Finish Grey, Matt - slight sheen, rough
Packing Base 20 liter 4 liter
Hardener 5 liter 1liter
Salt Spray Resistance 92% zinc content- more than 500 hrs.

APPLICATION
Remove oil, grease and other contaminants using proper degreasing agent. For severe corrosive conditions blast clean the surface. Special care must be taken on weld areas to remove flux & spatter. The cleaned surface should be coated before it gets contaminated or applies wash primer before subsequent coat of zinc rich primer.
Stir base thoroughly then mix three parts base and one part hardener by volume to uniform consistency. Allow the mixture to mature for 20-30 min. and stir again before application & occasionally during use to prevent settling of metallic zinc.
For Brush, Roller, Airless spray application, no thinning is required. In conventional spraying, 5% to 10% thinning is recommended for ease of application.

NOTE
1) Use the mixed paint within specified pot life period
2) Do not apply at temperatures below 10°C or at high relative humidity, above 90% or during rain, fog or mist.
3) Brushes & spray equipment should be cleaned with Thinner EP-102 otherwise equipment is liable to be damaged.


Epoxy Primer High Build Zinc Rich

Go Back to - Home / Products

Introduction -

Tuff Coat H.B. Epoxy Zinc rich primer is a two- pack system enriched with metallic zinc to provide outstanding performance in highly corrosive environment. Metallic Zinc imparts cathodic protection to the base metal and Epoxide groups react with polyamide/ Amine adduct hardener to form tough, non-convertible film at ambient temp or elevated temp. It resists photo degradation by UV light as it contains UV absorber.

RANGE OF APPLICATION
Suitable for application as a priming coat on structural steel, pipelines, and tank exteriors of refineries, power generation plants, mining facilities bulk handling equipment and fertilizer industries etc. This can be TOP-COATED with Epoxy Paints; Polyurethane paints chlorinated rubber paints for specific applications.

KEY PROPERTIES
1. Provides excellent adhesion on blast cleaned steel work
2. Withstands 200°C dry heat
3. Builds high DFT in single coat
4. Excellent corrosion resistance
5. With suitable TOP-COAT it resists most salts & alkalis
6. Mild Acid & alcohol resistance (Direct immersion is not advisable)
7. Resists splash, spillage, immersion of aromatic hydrocarbon & solvents
8. Good abrasion resistance

PRODUCT DATA (Two types available)
Zinc Dust Content 92%
Mixing ratio by Volume Base: Hardener 4: 1
Pot Life 3 - 4 hrs.
Individual shelf life Up to 1 year months in sealed condition & at ambient temp.
Application By Brush, Airless spray, Roller or Conventional
Covering Capacity (Theoretical)
(Practical)
6.5 - 7 sq. m. / Lit.
4.5 - 6 sq. m / Lit.
Drying time at room temp Tack free - 1.5 hrs
Hard dry - overnight
Full cure time - 7days
Overcoat Interval Minimum overnight
Max. Recommended DFT 120-140 µ in single coat.
Stoving schedule (if necessary) 120°C./30 min
Flash Point above 22°C
Thinner / cleaner TUFF COAT THINNER EP-102
Finish Grey, Matt - slight sheen, rough
Packing Base 20 liter 4 liter
Hardener 5 liter 1liter
Salt Spray Resistance 92% zinc content- more than 400 hrs.

APPLICATION
Remove oil, grease and other contaminants using proper degreasing agent. For severe corrosive conditions blast clean the surface. Special care must be taken on weld areas to remove flux & spatter. The cleaned surface should be coated before it gets contaminated or apply wash/etch primer before subsequent coat of zinc rich primer.
Stir base thoroughly then mix four parts base and one part hardener by volume to uniform consistency. Allow the mixture to mature for 20-30 min. and stir again before application & occasionally during use to prevent settling of metallic zinc.
For Brush, Roller, Airless spray application, no thinning is required. In conventional spraying, 5% to 10% thinning is recommended for ease of application.

NOTE
1) Use the mixed paint within specified pot life period
2) Do not apply at temperatures below 10° C or at high relative humidity, above 90% or during rain, fog or mist.
3) Brushes & spray equipment should be cleaned with Thinner EP-102 otherwise equipment is liable to be damaged.
TUFF COAT EPOXY ZINC RICH priming is also known as "COLD GALVANISING"

Reach us

Contact Details

Tuff Coat Polymers Pvt. Ltd.

S. No. 39, 1133, Manikbaug, Vadgaon (Bk.), Sinhagad Road, Pune - 411 051, Maharashtra, India.

Tel No.: +91 - 20 - 24351394 / 24353137

Cell No.: +91 98227 62122