Epoxy Paint Coal Tar (Black)

Go Back to - Home / Products

Introduction - This system is based on low molecular weight epoxy resin with high solid content cured with suitable polyamide or Amine Adduct. This system gives excellent performance in highly chemical & most severe Corrosive environment. System is unaffected by alkalinity or sulphates in soil water & suitable for use in conjunction with cathodic protection. The high film thickness reduces the required number of coats.
Recommended Use: - On structural steel, pipelines, chemical plants, water proofing areas, coastal installations, ship bottom, etc.

Type Two Pack
Base Epoxy Resin suitably pigmented & blend of Coal Tar pitch
Hardener Polyamide with catalyst / Amine Adduct
% NVM of system Minimum 52 - 55 %
Mixing Ratio 3:1 by Volume
Pot life of Mixture (1:1) 3 - 4 Hours
Application By Brush, Roller, Air-less Spray.
Recommended DFT 35 - 45 Microns
Covering Capacity 6 - 7 Sq. Mtr. / Liter theoretical by spray
Drying Time Surface Dry - 30 - 40 minutes Maximum
Tack Free - 3 - 4 Hours Max
Hard Dry - 24 Hours
Full Curing 7 Days
Over Coating Interval 24 Hours Minimum 7 Days Maximum
Colour Black to Grayish black
Packing 10 & 20 Liters
Flash Point Above 25°C
Thinner / Cleaner TC/EP-102
Finish Semi gloss & smooth
Storage Up to 8 months in packed condition at normal room temp.
Temp. Resistance 120°C Dry heat
Alkalis & Detergents Unaffected (Direct immersion not recommended)
Alcohol's Resist to splash & spillage.
Acids Resist to splash & spillage & fumes
Salts Withstand continues immersion in mild alkalis or neutral salt solutions (direct immersion in concentrated acid salts is not recommended)

Application -Before application of topcoat EP-102 Epoxy Coal Tar do all necessary pretreatment of the job. For M. S. surface, remove grease oil and other contamination by using proper degreasing agent. Blast clean the surface for heavy rusting or remove with de-rusting chemicals to clean the surface. For old concrete, remove all salt deposition/fungal growth, loosely bound coatings, and dust particles and make the surface rough. Also for new concrete coating do the needful pretreatment, priming and then apply topcoat EP-101 Epoxy Coal Tar. Use EP-101 Epoxy Primer Red Oxide Zinc Phosphate or Zinc Rich Primer before applying the topcoat. Stir the base component thoroughly and mix three parts of base and one part of hardener by volume to uniform consistency. Allow it for intermediate reaction for 15 - 30 min for stabilization and stir again before use. Make required viscosity as per application method with TC/EP-102 thinner.

The pot lifetime is only 3 - 4 Hrs. Mix the materials as per requirement. Close the containers immediately, to avoid the chances of moisture absorption in material and solvent losses. Do not apply in humid condition, during raining or mist and fog or at very low temperature below 10° - 12° C.


Epoxy Paint Coal Tar High Build

Go Back to - Home / Products

Introduction - This system is based on medium molecular weight epoxy resin cured with suitable polyamide or Amine Adduct. This system gives excellent performance in highly chemical & most severe Corrosive environment. System is unaffected by alkalinity or sulphates in soil water & suitable for use in conjunction with cathodic protection.

Recommended Use: - On structural steel, pipelines, chemical plants, waterproofing areas, coastal installations, ship bottom, etc.

Type Two Pack
Base Epoxy Resin suitably pigmented & blend of Coal Tar pitch
Hardener Polyamide with catalyst / Amine Adduct
% NVM of system Minimum 85 %
Mixing Ratio 4:1 by Volume
Pot life of Mixture (1:1) 2 - 3 Hours
Application By Brush, Roller, Air-less Spray.
Recommended 75 - 80 Microns
Covering Capacity 3.5 - 5 Sq. Mtr. / Liter
Drying Time Surface Dry - 4 - 6 Hours Maximum
Tack Free - 10 - 12 Hours Max
Hard Dry - More than 72 Hours
Full Curing 7 Days
Over Coating Interval 24 Hours Minimum 7 Days Maximum
Colour Black to Grayish black
Packing 10 & 20 Liters
Flash Point Above 30°C
Thinner / Cleaner TC/EP-102
Finish Semi gloss & smooth
Storage Up to 8 months in packed condition at normal room temp.
Weatherability Good in most environments
Temp. Resistance 150°C Dry heat
Alkalis & Detergents Unaffected (Direct immersion not recommended)
Solvent Resistance (Aliphatic-Aromatic) Withstand to splash & spillage.
Alcohol's Resist to splash & spillage.
Acids Resist to splash & spillage & fumes
Salts Withstand continues immersion in mild alkalis or neutral salt solutions (direct immersion in concentrated acid salts is not recommended)

Application - Before application of topcoat EP-102 Epoxy Coal Tar do all necessary pretreatment of the job. For M. S. surface, remove grease oil and other contamination by using proper degreasing agent. Blast clean the surface for heavy rusting or remove with de-rusting chemicals to clean the surface. For old concrete, remove all salt deposition/fungal growth, loosely bound coatings, and dust particles and make the surface rough. Also for new concrete coating do the needful pretreatment, priming and then apply topcoat EP-101 Epoxy Coal Tar. Use EP-101 Epoxy Primer Red Oxide Zinc Phosphate or Zinc Rich Primer before applying the topcoat. Stir the base component thoroughly and mix four parts of base and one part of hardener by volume to uniform consistency. Allow it for intermediate reaction for 15 - 30 min for stabilization and stir again before use. Make required viscosity as per application method with TC/EP-102 thinner.

The pot lifetime is only 3 - 4 Hrs. Mix the materials as per requirement. Close the containers immediately, to avoid the chances of moisture absorption in material and solvent losses. Do not apply in humid condition, during raining or mist and fog or at very low temperature below 10° - 12° C.

Reach us

Contact Details

Tuff Coat Polymers Pvt. Ltd.

S. No. 39, 1133, Manikbaug, Vadgaon (Bk.), Sinhagad Road, Pune - 411 051, Maharashtra, India.

Tel No.: +91 - 20 - 24351394 / 24353137

Cell No.: +91 98227 62122